DPFs are designed to capture the harmful particulates such as soot and ash before they are released into the atmosphere, and keep the air cleaner and safer.
But the ceramic filters are not easy to install or replaced, so we produce a specialized DPF package, kit to make the process simpler and more efficient. it is a valuable product for the aftermarket customers all over the world. It is compatible with a wide range of diesel engines, making it a universal solution for aftermarket.
Honmat DPF package includes ceramic substrate, support mat, metal shell, ring clamps, gaskets etc.. It is made of high-quality materials, such as stainless steel and silicone or cordierite, which ensure the tensile strength, reliability and durability.
The DPF package design is facilitated in installation for the maintenance personnel even without prior experience or instruction. Thus, the cost of replacing a damaged DPF will be reduced significantly by using Honmat DPF package.
In one word, Honmat DPF package is a valuable product for aftermarket merchants, with high capture effectiveness, excellent performance on reliability and durability, operation easy and simple when replace the damaged DPFs.
Product Dimension Specification
| Test Item | Units | 100CPSI | 200CPSI | 300CPSI | 300CPSI(ACT) | |
| Cell Density | CPSI | 100±5 | 200±10 | 300±15 | 300±15 | |
| Wall Thickness | mil | 15.00 | 12.00 | 10.00 | 9.00 | |
| mm | 0.40±0.03 | 0.32±0.03 | 0.25±0.03 | 0.23±0.03 | ||
| Diameter(≤120mm) | mm | ±1.0 | ±1.0 | ±1.0 | ±1.0 | |
| Diameter(＞120mm) | mm | ±1%*D | ±1%*D | ±1%*D | ±1%*D | |
| Height(≤200mm) | mm | ±1.0 | ±1.0 | ±1.0 | ±1%*D | |
| Height(＞200mm) | mm | ±1%*L | ±1%*L | ±1%*L | ±1%*L | |
| Perpendicularity(H≤100mm) | mm | Max 1 | Max 1 | Max 1 | Max 1 | |
| Perpendicularity(H＞100mm) | mm | Max 1%*H | Max 1%*H | Max 1%*H | Max 1%*H | |
| Parallelism(D≤100mm) | mm | Max 0.6 | Max 0.6 | Max 0.6 | Max 0.6 | |
| Parallelism(D＞100mm) | mm | Max 0.6%*D | Max 0.6%*D | Max 0.6%*D | Max 0.6%*D | |
| Weight | g/L | 540±80 | 520±60 | 440±60 | 440±60 | |
Materials and Properties Specifications:
| Test Item | Units | 100CPSI | 200CPSI | 300CPSI | 300CPSI(ACT) | |
| Chemical Composition | SIC | % | 78±5 | |||
| Si | % | 11±4 | ||||
| SiO2 | % | 11±5 | ||||
| Compressive Strength | A-aix | Mpa | Min 8.0 | |||
| Isostatics Strength | Mpa | Min 1.0 | ||||
| CTE(25℃～800℃) | cm/cm/℃ | Max 5.5x10-6 | ||||
| Porosity | % | 41±5 | ||||
| Median Pore Diameter | μm | 11±3 | ||||
| Thermal Shock Resistance | ℃/Time | 450 Three times | ||||
| Softening Temperature | ℃ | Min 1600 | ||||
Origin: China
Price: Negotiable
Shape：Customized
Packing: export standard
Sample provision: Negotiable
MOQ: Customized size 10 pieces